| Product |
FA69 |
|
| 试验项目 |
试验方法 |
测试数据 |
| ASTM |
测试条件 |
| 熔融指数[g/10min] |
D1238 |
220 ℃, 10.0㎏ |
15-20 |
拉伸强度
[Kg/cm2] |
D638 |
50mm/min 23 ℃ |
380-450 |
| 伸长率[%] |
D638 |
23 ℃ |
20-90 |
| 弯曲强度[Kg/cm2] |
D790 |
23 ℃ |
480-520 |
弯曲弹性率
[Kg/cm2] |
D790 |
23 ℃ |
20000-22500 |
| Izod 缺口冲击强度[kg.cm/cm] |
D256 |
6.4mm, Notched,23 ℃ |
38-45 |
| 热变形温度 [℃] |
D648 |
120℃/h,1.82Mpa |
80-82 |
| 成型收缩率[%] |
D955 |
|
0.4-0.7 |
| 比重 |
D792 |
23℃ |
1.04±0.02 |
| 阻燃性 |
UL94 (*) |
1/8"(3.2mm) |
HB |
| 特性 |
超高耐冲击性 |
| 用途 |
电话、玩具、手提箱、缝纫机、冰箱、洗衣机、汽车零配件等 |
|
|
|
|
 |
|
|