| HHIPS |
| |
FH-50R |
FH-50R
| 试验项目 |
试验方法 |
测试数据 |
| ASTM |
测试条件 |
| 熔融指数[g/10min] |
D1238 |
200 ℃, 5.0㎏ |
10-15 |
拉伸强度
[Kg/cm²] |
D638 |
50mm/min 23 ℃ |
200-280 |
| 伸长率[%] |
D638 |
23 ℃ |
50-80 |
| 弯曲强度[Kg/cm²] |
D790 |
23 ℃ |
600-750 |
弯曲弹性率
[Kg/cm²] |
D790 |
23 ℃ |
20000-21000 |
| Izod 缺口冲击强度[kg.cm/cm] |
D256 |
6.4mm, Notched,23 ℃ |
10-11 |
| 热变形温度 [℃] |
D648 |
120℃/h,1.82Mpa |
75-78 |
| 成型收缩率[%] |
D955 |
|
0.3-0.6 |
| 比重 |
D792 |
23℃ |
1.18±0.02 |
| 阻燃性 |
UL94 (*) |
1/8"(3.2mm) |
V0 |
| 特性 |
阻燃 |
| 用途 |
电视机外壳、办公用品、家电零件外壳 |
|
|
 |
|
|