| 阻燃PP |
| |
FP01R2 |
FP20R2 |
FP20R0 |
FP01R2
SGS报告
|
试验项目
|
试验方法
|
测试数据
|
|
ASTM
|
测试条件
|
|
熔融指数[g/10min]
|
D1238
|
230 ℃, 2.16㎏
|
20-35
|
拉伸强度
[Kg/cm2]
|
D638
|
50mm/min 23 ℃
|
250-350
|
|
伸长率[%]
|
D638
|
23 ℃
|
30-80
|
|
弯曲强度[Kg/cm2]
|
D790
|
23 ℃
|
240-320
|
弯曲弹性率
[Kg/cm2]
|
D790
|
23 ℃
|
700-1200
|
|
Izod 缺口冲击强度[kg.cm/cm]
|
D256
|
6.4mm, Notched,23 ℃
|
5-11
|
|
热变形温度 [℃]
|
D648
|
120℃/h,0.45Mpa
|
110-135
|
|
成型收缩率[%]
|
D955
|
|
1.1-1.25
|
|
比重
|
D792
|
23℃
|
0.90-0.98
|
|
阻燃性
|
UL94 (*)
|
1/8"(3.2mm)
|
V2
|
|
特性
|
高光泽
|
|
用途
|
中空板、微发泡管、线圈骨架、蓄电池壳体、电器壳体、保险丝盒、壁炉面板
|
FP20R2
SGS报告
|
试验项目
|
试验方法
|
测试数据
|
|
ASTM
|
测试条件
|
|
熔融指数[g/10min]
|
D1238
|
230 ℃, 2.16㎏
|
10-35
|
拉伸强度
[Kg/cm2]
|
D638
|
50mm/min 23 ℃
|
250-350
|
|
伸长率[%]
|
D638
|
23 ℃
|
30-80
|
|
弯曲强度[Kg/cm2]
|
D790
|
23 ℃
|
250-400
|
弯曲弹性率
[Kg/cm2]
|
D790
|
23 ℃
|
700-1100
|
|
Izod 缺口冲击强度[kg.cm/cm]
|
D256
|
6.4mm, Notched,23 ℃
|
5-11
|
|
热变形温度 [℃]
|
D648
|
120℃/h,0.45Mpa
|
110-135
|
|
成型收缩率[%]
|
D955
|
|
1.1-1.20
|
|
比重
|
D792
|
23℃
|
0.95-1.04
|
|
阻燃性
|
UL94 (*)
|
1/8"(3.2mm)
|
V2
|
|
特性
|
高光泽
|
|
用途
|
中空板、微发泡管、线圈骨架、蓄电池壳体、电器壳体、保险丝盒、壁炉面板
|
FP20R0
SGS报告
|
试验项目
|
试验方法
|
测试数据
|
|
ASTM
|
测试条件
|
|
熔融指数[g/10min]
|
D1238
|
230 ℃, 2.16㎏
|
6-15
|
拉伸强度
[Kg/cm2]
|
D638
|
50mm/min 23 ℃
|
250-350
|
|
伸长率[%]
|
D638
|
23 ℃
|
30-80
|
|
弯曲强度[Kg/cm2]
|
D790
|
23 ℃
|
280-350
|
弯曲弹性率
[Kg/cm2]
|
D790
|
23 ℃
|
1200-1800
|
|
Izod 缺口冲击强度[kg.cm/cm]
|
D256
|
6.4mm, Notched,23 ℃
|
7-11
|
|
热变形温度 [℃]
|
D648
|
120℃/h,0.45Mpa
|
110-120
|
|
成型收缩率[%]
|
D955
|
|
1.0-1.10
|
|
比重
|
D792
|
23℃
|
1.05-1.3
|
|
阻燃性
|
UL94 (*)
|
1/8"(3.2mm)
|
V0
|
|
特性
|
高刚性
|
|
用途
|
中空板、微发泡管、线圈骨架、蓄电池壳体、电器壳体、保险丝盒、壁炉面板
|
|
|
 |
|
|